海韵牌BT-9019型磷酸盐高铝耐火砖Chaton brand BT-9019 type high aluminum phosphate brick 我公司生产的普通磷酸盐砖、耐磨砖、高荷软砖、钢纤维砖均采用**重烧高铝矾土为主要原料，再添加各种辅助材料及各种结合剂，经高吨位压砖机成型，具有体密大、耐磨性好、高温强度大，抗压、抗折度高、抗剥落性能好及抗化学侵蚀耐磨性能好等特点。 Our company produces the ordinary phosphate brick, wear-resisting brick, GaoHe soft bricks, steel fiber brick adopts high-quality refiring high bauxite as main raw materials, add various auxiliary materials and various binders, via high to
nnage pressure brick machine forming, with body density, good abrasion resistance, high temperature compressive strength, flexural degree is hig**nti-stripping performance is good and anti chemical etching wear-resisting performance is good wait for a characteristic. 产品主要用于水泥及其它热工窑炉中要求高温抗热震物料冲击频繁及长期摩擦的部位。 The product is mainly used in cement and other thermal shock resistance to high temperature of kiln material impact frequent and long-term friction parts.
| 牌号项目 | 磷酸盐砖 | 钢纤维砖 | 高荷软磷酸盐砖 | 兰晶石砖 |
| P | PA |
| AI2O3%，不小于 | 75 | 77 | 75 | 80 | 80 |
| Fe2O3%，不大于 | 1.2 | 1.2 | | 1.5 | 1.3 |
| 耐火度℃，不低于 | 1770 | 1770 | 1790 | 1790 | 1790 |
| 体积密度g/cm3，不小于 | 2.7 | 2.75 | 2.75 | 2.85 | 2.9 |
| 常温耐压强度MPa, 不小于 | 70 | 75 | 75 | 70 | 80 |
| 0.2MPa荷重软化开始温度℃，不低于 | 1350 | 1300 | 1380 | 1510 | 1550 |
| 热震稳定性（1100℃水冷）次，不小于 | | | 35 | 20 | 25 |
海韵牌BT-9019A型**高铝耐火砖Chaton brand BT-9019A the high-quality aluminum refractory bricks 9019A type
| 牌号项目 | 抗剥落高铝砖 | 耐碱砖 |
| 高强型 | 隔热型 |
| AI2O3%，不小于 | 70 | 20～30 | |
| Fe2O3%，不大于 | 1.5 | 2.0 | |
| SiO2% | 25 | 65～70 |
| 耐火度℃，不低于 | 1790 | 1650 |
| 体积密度g/cm3，不小于 | 2.5～2.6 | 2.25 | 1.65 |
| 显气孔率%，不小于 | 25 | 20 | 30 |
| 常温耐压强度MPa, 不小于 | 45 | 60 | 18 |
| 0.2MPa荷重软化开始温度℃，不低于 | 1470 | 1300 | 1250 |
| 热震稳定性，1100℃（水冷）次，不小于 | 30 | 10 | 5 |
| 重烧线变化PLC% | ±0.3 | -0.3～+0.1 | -0.4～+0.2 |
| 注：以上产品分别用于水泥回转窑的分解带、过渡带、窑门罩、冷却机高温区墙体及窑口等部位 |